Technical parameters:
1) JT/T280-2004 Standard
Physical Characteristics
Standard
Result
Appearance Colour: White/Yellow White/Yellow
Density (g/cm3): 1.8 ~ 2.3 2.02
Softening Point (oC): 90 ~ 125 103
Drying time of no sticking to wheel (minute) 3 max. 3
Luminance factor: White 75 min. 83
Yellow 45min. 51
Compression Strength(Mpa): 12 min. 18.10
Skid Resistance (BPN): 50 min. 55
Flow Resistance (%): 35±10 38
Glass Beads Content (%w/w): 18 ~ 25 22.6
Abrasion Resistance (mg 200r/1000g reduce weight): 80 max. 53.60
Flash Point (oC): 230oC min. 250 oC
2) BS3262
PHYSICAL CHARACTERISTICS:
SN Test requirements Specification Typical Results
White Yellow
1 Softening point ≥65℃ (Temperate grade) 67.5℃ 67℃
2 Density Approximtely 2.0 2.0 2.0
3 Flash point 235℃+ 235℃+
4 Luminance White：≥70%
Yellow：≥50% 79% 53%
5 Drying Time
at air temp 10+2℃,
at air temp 32+2℃
≤2 min (max)
≤10 min (max)
1 min
4.5min
1 min
4 min
6 Bond Strength ≥180PSI 280PSI 260PSI
7 Cracking Resistance (low temp) No crack No crack No crack
8 Flow Resistance ≤25% 13% 12%
9 Skid Resistance ≥45% 47% 47%
*Flash point carried out as a routine test to ensure safe handlling and melting during pre-heater and spraying operation.
3) AASHTO-M247
SN Test requirements Specification Typical Results
White Yellow
1 Softening point 102.5+9℃ 108℃ 107℃
2 Density 2.15 MAX 1.99 1.99
3 Flash point 240℃+ 240℃+
4 Day Light Reflectance after 4hs heat at 218℃ and cooled at 25℃+2 ℃ White：≥70%
Yellow：≥45% 79% 53%
5 Drying Time
at air temp 10+2℃,
at air temp 32+2℃
2 min (max)
10 min (max)
1 min
4.5min
1 min
4 min
6 Bond Strength 180PSI(min) 280PSI 260PSI
7 Cracking Resistance (low temp) No crack No crack No crack
8 Flow Resistance 21% MAX 13% 12%
9 Skid Resistance 45% MAX 48% 47%
*Flash point carried out as a routine test to ensure safe handlling and melting during pre-heater and spraying operation.
Packaging:
25kg compond-plastic bag
Standard:
1) JT/T280-2004 Standard
2) BS3262
3) AASHTO-M247
4) Other standards by requirements of clients
Additional Information:
TATU Brand Road marking Paints are made of high quality raw material, and its whole production processes are finished by completely automatic production line, absolutely avoid quality defects caused by artificial operation, such as large mixture ratio error, unstable quality, etc. and further make sure of high quality to customers. Please contact Henan TATU highway Co., Ltd if you require:
• Pricing and availability
• Or more specific information on this product or other products in the wide range of products manufactured by TATU Highway specifically for the road marking industry.